Institute of Metals Division - Further Studies of GPI Zone Formation in Al-2 At. Pct Cu

From variation in Young's modulus and Vicker's hardness during GPl zone formation in A1-2 at. pct Cu the following was observed: 1) the presence of grain boundaries does not have any perceptible? effect on the aging reaction; 2) the modulus charge is orientation dependent; 3) the activation energy for zone growth is confirmed to be 11 * 1 kcal per mole; 4) reaging after reversion is preceded by an incubation time that varies with temperature. An analysis is applied to the present data and to data of other workers and kinetic laws dependent on the quenching rate are determined. In Al-base Cu alloys the decomposition product of a supersaturated solid solution at low temperatures (for example 25°C) and the first product at moderate temperatures (for example 150oC) are Guinier-Preston zones of the first kind (GPI).' These zones are nonideal and are thought Jo 'Onsist roughly of sheets of Cu atoms up to 150A in diam and one or two atoms thick.' The kinetics of the reaction, ass — a2