Institute of Metals Division - Cr3O-Type Structure in V-Rh-Si, Nb-Rh-Si and Cr-Rh-Si Ternary Systems (TN)

The V-Rh-Si, Nb-Rh-Si, and Cr-Rh-Si systems were investigated to evaluate the extent of solid solubility between binary Cr3O structures. All Cr3O components lie within the favorable atomic size range1 for the formation of the Cr3O structure. Previous studies indicated complete solid solubility between V3Si and V3Sn2 and no solubility between Sn and cr3si3 or Si and Nb3Rh.4 The Cr3O structure is not found in the Cr-Sn and Nb-Si binary systems. Powder compacts were are-melted under argon, homogenized in a vacuum at 1000°C, and water-quenched. Alloys containing greater than 15 at. pet Si were annealed 100 hr. X-ray diffractometer methods were used to study all systems utilizing copper radiation for the Cr-Rh-Si system and chromium radiation for the other two systems. V-Rh-Si System. The alloys prepared in the V-Rh-Si system and the measured lattice parameters for the Cr3O structure found in each alloy are listed in Table I. The characteristic Cr3O diffraction pattern was found in all binary alloys. The measured lattice parameter of V3Rh (VRS-1) is in agreement with the reported value5 while the value for V3Si (VRS-5) is only in fair agreement.' In