Institute of Metals Division - A Method for Growing Bicrystals of Copper (TN)

In a study of grain boundary sliding in superpure Copper (99.999 pct),&apos; bicrystals of a specific shape were used, Fig. 1. That shape was adopted in order to minimize the deformation of grains on both sides of the boundary due to clamping. Another requirement was to obtain bicrystals with a rnicroscopically straight boundary, Fig. 2. Single crystals of predetermined orientation (growth axis parallel to <310>) were grown in a graphite mold from seed crystals. The apparatus for growing single crystals consisted of a vacuum system, argon purification train, vycor tube (in which a graphite mold was placed), a carriage for the induction coi1,and a Lepel (7-1/2 KW) high-frequency converter. The graphite mold was heated by induction and the charge in turn was heated by conduction. The induction coil was moved by means of a motor at a speed of 1 1/2 in. per hr. Single crystals of two different orientations were grown from the melt in one-half of a split graphite mold, Fig. 3(a). Two such crystals were then placed in contact with each other in another split mold, Fig. 3(b) using tapered inserts. The pair of crystals was then remelted starting 2 in. from the top to insure that the whole top portion of the crystals was maintained molten. By moving the induction coil