Influence of additives on microstructural changes of nitride bonded SiC refractories

In this paper microstructural development of nitride-Bonded SIC refractories is reported in presence of Al203, Mg() and Urea additives .The samples were prepared by mixing, shaping and firing at 1400-1500°c in a controlled atmosphere furnace. Phase analysis, microscopic observation and mechanical evaluation were taken for microstructural investigations. The strength of samples doped with Al203 was first increased and then decreased at higher amount of Al2O3 additions. The addition of MgO decreased the strength while the urea showed an improving effect on strength. These phenomena could be attributed to microstructural evolution and mainly to liquid phase formation and grain morphology. It was found that the additives such as Al203, MO and urea could modify the microstructure in terms of phase formation and texture modification, which in terms influences the mechanical behavior.