In-Flight Thermal Plasma Processing Of Ilmenite For Production Of Tio2 Rich Slag And Pig Iron

Mineral ilmenite is a major resource for titanium, whose major application is for production of Titanium dioxide (TiO2) for pigment application. The production of pigment grade TiO2 from ilmenite was earlier carried out by acid leaching, which has now been banned due to environmental regulations. Further acid leaching leads to loss of iron metal values as sulphate or chloride which are also treated as effluent. In thermal plasma processing the metal values are recovered as high value pig iron and Titanium dioxide is recovered as Titania rich slag containing 80 to 85 percent TiO2. The Titania rich slag has now been considered as a better input material than synthetic rutile for production of pigment grade Titanium dioxide. On the other hand, high value pig iron goes for automobile industry for specific application. An Inflight-flight Thermal Plasma Processing plant, used for the production of Titania Rich slag and high value Pig iron from ilmenite, with 20kg capacity was designed and fabricated. The reactor has the provision to utilize the flue gas generated for preheating the input of raw materials. Various aspects of designing the furnace operation include viz. Feeding the raw material at a fixed rate, designing the crucible used for melting ilmenite, proper cooling arrangements, an innovative method for tapping the melt, recovery of heat from the gases, various safety arrangements which are some of the important milestone of the present work. The various operations have been carried out through a controller panel. Experiments were carried out to optimize various processing parameters using statistical modeling. Large scale experiments have been carried out at 10 to15 kg scale. The material balance has been calculate, and it has been observed, that about 95 percent recovery could be obtained for both Iron and Titanium oxide from ilmenite. The detailed characterization on Titania rich slag and iron has been carried out. It has also been shown that using the above slag, it is possible to prepare nanosized Titanium dioxide powder containing about 98 percent Titanium dioxide by optimizing leaching conditions. Keywords: titania rich slag, ilmenite, thermal plasma