Improving Corrosion Resistance of Mg/Mg2Si Composite by Addition of Bi

Magnesium matrix composites are widely used in automotive and aerospace industries for achieving higher performance due to their light weight. The Mg2Si intermetallics compound in Mg/Mg2Si composite exhibits many excellent properties such as high melting temperature, high hardness, and low thermal expansion coefficient. However, under normal cast conditions, the primary Mg2Si phase exhibits coarse Chinese script or dendritic morphologies and the eutectic structures is very brittle resulting in the low ductility and strength of the alloys. Modification treatment is a very effective method to obtain fine microstructure and improve the mechanical properties of the alloys due to low production cost. In this investigation various amount of bismuth addition have been carried out on Mg?5wt %Si alloy to refine and modify the morphology of coarse Mg2Si in order to improve the corrosion resistance of the composite product. The effect of Bi content on microstructure of Mg2Si/Mg composite was investigated by optical and scanning electron microscopy followed by EDX analysis and X-Ray diffraction. In order to compare corrosion resistance of unmodified and modified specimens, Immersion test and potentiodynamic polarization (PD) were used. The results showed that by Bi addition, the size of primary phase Mg2Si was considerably reduced and the morphology was modified from a coarse dendritic shape to a polyhedral shape. The results also indicated that the corrosion resistance of Mg?Si alloys was improved by the addition of 1%wt of Bi due to the reduction, refinement and evenly distribution of Mg2Si phase. Indeed, both the morphology and distribution of Mg2Si intermetallic had a great influence on the corrosion behavior of Mg/Mg2Si composite.