Hot Workability of M42 Tool Steel Additionally Alloyed with CO and MO

"Hot deformability of M42 tool steel additionally alloyed with cobalt and molybdenum was investigated. Hot-compression tests were carried out in the temperature range 850 °C -1200 °C, at strain rates range 0.001--6s-l up to strain of0.9. Field-emission scanning electron microscope and optical microscopy were used for characterization of microstructure of deformed samples, which revealed a very complex precipitation of carbides that strongly depends on the soaking temperature, the soaking time, the stress state, the deformation temperature as well as on the strain rate. Gathered data was used to calculate the processing parameters such as process maps, apparent activation energies and strain hardening exponents. For better understanding of thermodynamical properties of the studied steel a simultaneous thermal analysis was conducted. Furthermore the analysis of phase equilibrium was calculated using Thermo-Cale software. On the basis of these studies the optimal soaking temperature and process windows were determined.IntroductionHot workability ofledeburitic tool steels is important economic factor. This means that for each tool steel individuallysafe range of hot working parameters should be revealed. Publications in the literature with regard to the hot workability of tool steels are rare and therefore more information from this research area is desired.The relatively low hot workability of ledeburitic tool steels, i.e. steels in which the solidification is completed by a eutectic transformation of the residual interdendritic liquid to austenite and various alloy carbides (ledeburitic carbides), is usually characterized by the production of surface and internal cracks during the hot deformation."