Horizontal Directional Solidification of Zn-Al Alloys

"Zinc-Tin alloys were solidified in horizontal form and the obtained results were analyzed. During solidification the distribution of temperatures were measured by using thermocouples located strategically along the length of the samples. From the measured temperatures the following parameters were derived; the local temperature gradient, the cooling rate and the velocities of the liquid and solids fronts. Comparing the structure of the samples and the values of these parameters it was found that the temperature gradient reaches minimum values of as low as - 0.6 °C/cm, and velocities of the fronts of around 0.1 cm/s. In addition, the grain size was measured along the samples. The results are presented and discussed in the frame of the results previously obtained for other alloys.IntroductionGenerally solidification leads to two types of grain morphologies: columnar and equiaxed. The origin of each one has been the subject of numerous theoretical and experimental researches in the field of metallurgy for many years [1-7]. The columnar-to-equiaxed transition, CET, is considered as an object of high technological relevance with respect to the directional solidification of metallic alloys. This structure transition may be sharp or gradual and it has been reported to be dependent on thermal conditions associated with the casting process, including melt convection, heat transfer coefficients at the metal-mold interface, growth rates, thermal gradients, cooling rates, transport of solute, alloy composition, melt superheat, mold temperature, mold design, casting size, casting geometry, and the concentration of nucleating particles. As a consequence, it is critical for industrial applications to understand the physical mechanisms which control this transition during solidification. Many studies highlight the importance of the relative growth of the equiaxed and columnar grains and develop expressions or numerical procedures to describe a criterion for the CET. A number of experimental investigations reported in the literature suggest that the CET occurs when GL in the melt reaches a minimum critical value [5-7]."