Graphite

The first use of graphite is lost in the mists of time. It was used by primitive man to make drawings on the walls of caves and by the Egyptians to decorate pottery. As early as 1400 A.D. graphite crucibles were being made in the Haffnerzell district of Bavaria. Through the Middle Ages graphite was confused with other minerals, especially galena and molybdenite. Two common names that are still used for the mineral are "Plumbago," meaning leadlike, and "Black Lead." The latter name implied that graphite is either composed of lead or at least contains a large percentage of it. Gessner is credited with having recognized it as a separate mineral in 1565, but its composition was not determined until 1779, when Scheele demonstrated that graphite oxidized to carbon dioxide, thus proving its carbon constitution. In 1789, Werner named it "graphite" from the Greek word "graphein," meaning to write. The United States has long relied on foreign countries for its graphite supplies. This reliance has been due more to the lack of suitable domestic graphites than to any particular preference for buying minerals overseas. Ceylon (now Sri Lanka) graphites were imported as early as 1820, and Madagascar graphites have been imported since the properties on that island were opened up about a hundred years later. Mexico has long supplied the United States with most of its requirements for amorphous graphite. Physical Properties and Classification Graphite is found in laminated, flaky aggregates disseminated in schistose rocks. It also occurs in veins and exhibits a foliated or fibrous structure. Graphite is a black lustrous mineral that crystallizes in the hexagonal system, with rhombohedral symmetry. The crystals have tabular form and are six-sided; the faces are commonly striated. The flakes have perfect basal cleavage and are opaque. When well crystallized, the flakes have a black metallic luster while the amorphous material is black and earthy, with a microcrystalline compactness. The flakes feel greasy. Graphite is an excellent conductor of heat and electricity. It melts at approximately 3500°C and sublimes at about 4500°C. It is combustible in the presence of oxygen between 620° and 670°C, but is stable and chemically inert at ordinary temperatures.