Experiments With Sherardizing

WHEN clean iron and metallic zinc dust, protected from the air, are heated below the melting point of zinc, the iron takes on a coating that has excellent protective value. This coating is a brittle alloy of zinc and iron, and the process is called sherardizing. Although the zinc particles are covered with oxide and cannot touch the iron, an extremely small amount of the zinc vaporizes and the vapor, reaching the iron, alloys with it. Other zinc then vaporizes to replace that which has been removed from the atmosphere. This process continues indefinitely at a decreasing rate, for the coating already formed permits zinc to diffuse through-it to combine with the iron beneath. In this way, the coating grows outward from the surface of the iron, as the bark grows from a tree. The method of growth was clearly seen while sherardizing small cubes of cast iron, at about 450° C., in a small glass-stoppered bottle enclosed in a rotating drum. The dust contained about 3 per cent. iron, which prevented caking, and coatings 1/2 in. thick were grown in a few hours. After a heavy layer had been formed, the cubes were again: treated for a shorter time. The layer last formed was seen to lie next to the iron, instead of at the outer surface, showing that the growth was from the surface of the iron outward. The coatings split at the edges and corners, leaving the iron exposed there. Flakes of graphite from the iron were lifted upward and embedded in the coatings. The composition of sherardized coatings varies from the outer surface inward, as would be expected from the mode of growth. That is, the iron content increases slowly at first, then more rapidly as the iron is approached. At the surface the least amount of iron possible is 6 per cent., as the experiments described below have shown.