End-Of-Life Mode Of Failure Of A Zinc Sulphide Concentrate Fluidised Bed Roaster And Its Rebuilding

Zincor operates four Lurgi fluidised-bed roasters at its roast-leach-electrowin refinery in Springs, South Africa. In 2006, Zincor?s four roasters had reached ages ranging between 26 and 38 years, while the expected life of this type of roaster is generally 20 to 25 years. Based on its condition, Roaster 3 was the first to be rebuilt in 2006. Roaster 4 is being rebuilt in 2007 and the last two roasters will be rebuilt over the next few years as necessary. The main damage to Roaster 3 was caused by buckling of the roaster steel shell. This caused the freeboard and dome areas to shift, resulting in cracks in the dome brick lining and crumbling of the bricks lining the freeboard. The steel shell buckled due to the combined effects of too-high operating temperatures and corrosion caused by the following two main factors: ? Thicker external insulation was installed during a previous maintenance shut which resulted in and increased steel shell temperature and exacerbated the normal metal fatigue; ? SO2/SO3 containing gas that had permeated through the brick lining, passed through its dew point during frequent planned and unplanned shuts over the life of the roaster. This caused acid formation between the refractory brick lining and steel shell, resulting in corrosion of the shell. The initial plan was to replace only the damaged areas of Roaster 3, but upon dismantling more damage was found and the roaster was rebuilt from the tuyeres upwards. During the rebuild, the opportunity was taken to modify the design of some of the brickwork to extend its life and make future repairs easier. This paper discusses the mode of failure of Roaster 3 and the lessons learnt during its dismantling and rebuilding.