Elemental Correlations And Distributions Of KODOS Ferromanganese Nodules, Focused On SiO2 And CaO

Although Mn, Fe, Cu, Ni, and Co have been the main interests since the ferromanganese nodules had been found, the other major components such as Si and Ca might be very important controlling factors in the processing due to the locally variable content. It is because of the fact that SiO2 and CaO are added to decrease the smelting temperature in the reduction-smelting method for manganese nodule processing. We have compiled the 707 chemical data for KODOS (Korea Deep Ocean Survey) ferromanganese nodules, which have been acquired from 1994 to 2001 and have been also standardized from 2001 to 2003 to avoid the discrepancy between the data sets. All 707 chemical data were used for the hierarchical cluster analysis to get the elemental correlations and also classified by the morphological types. The averages from each station were classified by the facies groups (Fig. 1) and the localities. Then all data are plotted on the SiO2-CaO-MnO phase diagram at 1773°K to compare with the best compositional area in the nodule smelting. Variations and distributions of SiO2 and CaO as well as those of Mn, Fe, Cu, Ni and Co in KODOS ferromanganese nodules were also reviewed. The mineral phases assigned by the cluster analysis are CFA (Carbonate Fluorapatite), Fe-oxide, Al-silicate, and Mn-oxide. MnO contents are generally higher than SiO2 contents in most of the morphological types except for the Is- and It-type. The Dt- and Tt-type show wider range and the E-types show high anomaly in their CaO contents. The stations which belong to facies group A and B show generally higher MnO contents than SiO2 contents, however, the stations of facies group C and D show wide range in their MnO and SiO2 contents.