Effect Of Temperature On The Solubility Of Iron Oxide In Iron

IRON oxide .(Fe0) plays an extremely important part in the manufacture of steel. In the open-hearth furnace and the Bessemer converter it is the chemically predominant compound and controls to a large extent both the operation of the furnaces and the composition and quality of their products. Almost all of the refining action is carried out through the medium of FeO, which oxidizes carbon, manganese, silicon, and phosphorus. At the end of any open-hearth or Bessemer heat the steel contains dissolved iron oxide, which must be wholly or partly eliminated. The type of deoxidation product depends on the amount of dissolved iron oxide and on the deoxidizer used. After the heat has been deoxidized and while it is being teemed, iron oxide diffuses from the ladle slag into the metal, causing losses of deoxidizer and increase in iron oxide content of the steel. It is generally believed that non-metallic inclusions are responsible for a great many failures of steel in service and for decreased yield of steel during rolling. The basis of most non-metallic inclusions is dissolved iron oxide. This investigation was undertaken in order to determine the amount of iron oxide that will dissolve in iron under various conditions. Steel-making slags are complex and it has been thought best to determine solubility under simple slags as a first step. The study is being continued under slags whose compositions approach those of operating. slags.