Effect of SiO2 Addition on Reduction of Fe-Si-Mn Alloy from Adjusted Converter Slag

"The present work studied the production of Fe-Si-Mn alloy from adjusted converter slag by thermodynamic analysis. The results showed that solubility of SiO2 in the molten slag increased with increment of temperature, and it is about 80% at 1800 ?. With increment of SiO2 content, a(MnO) and a(CaO) decreased, and a(FeO) increased to the maximum when w(SiO2) is about 30%. As a result, the reduction of the slag was in the order of Fe?Mn?P before SiO2 reduction, the reduction order was Fe?P?Mn?Si when SiO2 content in the slag was from 46.4% to 54.2%, and changed to Fe?Si?P?Mn when SiO2 content exceeded 54.2%. The mass fraction of Si in the alloy phase increases with increasing of w(SiO2) in the slag, and the mass fraction of Si in the alloy reached to 62.2% at 1800 ?.IntroductionFerroalloy production is a high energy consumption and high pollution industry[1-2]. If ferroalloy production could be produced from molten slag by addition of carbon-reducing agent, the valuable metal and oxide in the slag can be recycled, most importantly, if the high-temperature resource carried by molten slag can be made full use in the field of ferroalloy production, the power consumption of ferroalloy production could be cut down greatly.Converter steel slag is a kind of byproduct in steelmaking processing increasing rapidly with the increment of crude steel, but the utilization ratio is low. Most heat recovery research is still in the experimental stage except the heat recovery of blast furnace slag by water quenching method, at present[3-4]. It is of great significance for enterprises to energy saving and emission reduction if the molten steel slag could be utilized directly. Not only the reuse methods of liquid steel slag material can be promoted, but also the use of heat carried in the slag could be achieved. The basicity of converter slag is high and the activity of SiO2 is low so the reduction of SiO2 in the slag is little. The compositions of slag and metal phases were calculated by Factsage program on different conditions to explore the reduction of converter slag for recovery of valuable metals and an efficient new way to use the high-temperature heat combining with the current reuse and research status of converter slag. Further, the improvement of components activity in slag and the increase of Si concentration in the metal were also dicussed."