Effect of Reduction Conditions on Pre-Reduction Behaviors of Self-Fluxed Pellets in Corex Process

"In order to produce high quality metalized products and prevent from burden cohesion during pre-reduction, self-fluxed pellets were made for COREX process in the paper. The effects of reduction temperature and reducing gas composition on pre-reduction behaviors of self-fluxed pellets are studied. The results show that the prereduced pellets have poor quality and deposited carbon appears when the reduction temperature is between 600°C and 700°C. The metallization rate, reduction degree and compressive strength of prereduced pellets are promoted by the elevating reduction temperature and mole fraction of H2. Pellets reduced by pure H2 at 800°C have high metallization rate (96.2%), reduction degree (99.4%) and compressive strength (960N/pellet). In all tests, self-fluxed pellets display normal swelling (RSI<l5%) behavior which reveals that self-fluxed pellets are suitable for COREX process. Increasing reduction temperature and mole fraction ofH2 in reducing gas is benefit for pre-reduction of pellets.IntroductionCompared with Blast Furnace, the COREX process has advantages of short flow sheet, using non-coke coal and high-energy utilization. Acidic pellets and lump ores are the chief iron- bearing burden for COREX process which could lead to low melting point substance appearing in per-reduction process. In addition, the acidic hematite pellets tend to swell during the reduction [1-3]. This will result in decreasing compressive strength of pellets, burden cohesion, bad air permeability and poor work status in shaft furnace. Adding carbonate flux could restrain burden bonding to some extent in actual production, but decomposition of carbonate flux increases energy consumption. Worse still, weak reduction potential is unfavorable to iron material reduction [ 4, 5]."