Effect of Different Parameters on Breakouts in Billet Caster

"Breakouts are one of the biggest problems encountered during continuous casting of steel billets. Billets get cracked locally or break completely in two parts during solidification causing the liquid part of the partially solidified billet to empty inside the cooling chamber. Proper control of important parameters is necessary to avoid break outs during continuous casting. In the present work, the nature of the break outs at a billet caster at Tata Steel was studied. Data analysis was also done for certain casting parameters and the Sulphur tracer test was conducted to understand solidification in the mould. It was found that to reduce the occurrence of break outs, it was necessary to tune the operations based on the grade being cast and the design of the mould tube being used.IntroductionA break out during the continuous casting process is a rupture of the partially solidified shell inside the secondary cooling chamber, causing the contained liquid steel to spill out. In the mid 1970s while continuous casting technology was still in early stage of development, causes of breakouts was not well understood. Today, with technological development much has been understood about breakouts but, most of the understanding has been in the slab casting process wherein due to the higher level of instrumentation, a lot of information has been gained. In billet casting however, due to the geometry of the mould housing with the tube mould, multiplied by the complexity of the multiple strands, instrumentation has not been used and obtaining data for analysis has been difficult.Breakouts at billet casters are still the main hindrances to production. A break out results in a loss in production since the strand which has had a break out is now not available to produce and thus a six strand caster would be reduced to a five strand caster, increasing the time for casting the same tonnage. Additionally extra set up time is required as more often than not a mould change is required in order to have the strand casting again."