Effect Of Al2O3 Or Mgo Addition On Liquidus Of Feox Corner In Feox-SiO2-Caoslag At 1250 And 1300 °C

The FeOX-CaO-SiO2 base slag at intermediate oxygen partial pressures is very often used in non-ferrous smelting processes. This slag would also contain Al2O3 and MgO because these compounds are normal components in the ore and the refractory of a furnace. The objective of the present work is to determine the effect of Al2O3 or MgO addition on the liquidus temperatures of the plain FeOX-CaO-SiO2 slags in the atmosphere between intermediate pO2 of 10-6 and that of iron saturation at 1250 and 1300 °C. The experiments were carried out at given mass%CaO/(mass%CaO+mass%SiO2) ratios ranging from 0 to 1 and at spinel-tridimite double saturation. The experimental results show that the effect of Al2O3 or MgO addition on the plain FeOX-SiO2-CaO slag is not uniform and depends on the content of Al2O3 or MgO, the oxygen partial pressure and the mass% CaO/mass% SiO2 ratio. It is apparent that Al2O3 or MgO addition enlarges the spinel or wustite saturation area at almost all the oxygen partial pressures and temperatures of this research. The obtained phase diagrams will be useful in the metallurgical industry to assist in the selection of slag chemistry, operation condition and development of new processes.