Effect Of Al₂O₃ On Precipitation Behavior Of Phosphorus Enrichment Phase In Dephosphorization Slag

The precipitation behavior of phosphorus enrichment phase was investigated by slag modification with Al2O3. The mineral phase of the original slag and modified slags were measured by mineral phase microscope, SEM+EDS and XRD. The mechanism of Al2O3 modification was discussed according to the thermodynamic theory analysis software (Factsage version 6.3). The results show that the high phosphorus solid solution (nˊ2CaO·SiO2-3CaO·P2O5) was generated by the continuous reaction of nC2S-C3P (nˊ＜n) solid solution and Al2O3 under 1350℃. The amount of initially precipitated solid solution (nC2S-C3P) was reduced and even disappeared with the increasing of Al2O3. If the addition of Al2O3 is enough in the slag, the high phosphorus solid solution (nˊC2S-C3P) that generated by the above mentioned reaction will continue to react with Al2O3 to produce Ca2Al2SiO7 and even C3P, which was demonstrated that the addition of Al2O3 has a positive influence on the precipitation of phosphorus enrichment phase.