Development of Hypereutectic Al-Si Casting Alloys With Variable Mg Content

Conventional hypereutectic Al-Si alloys such as A390 are used principally for the casting of components used in wear applications requiring abrasive resistance such as in engine or compressor blocks. A comprehensive study was undertaken to investigate the potential of improving the mechanical properties of these alloys by the addition of magnesium. A thorough thermodynamic study of the effect of the addition of Mg to the conventional A390 alloy showed that Mg2Si starts to form as a primary phase at 4.2% Mg as well as in the products of the binary and ternary eutectic reactions forming the matrix. Experiments were carried out in producing castings with different cooling and solidification rates of alloys with up to 10% Mg. Mg additions were found to increase the hardness over the as cast alloy due to solid solution strengthening. Also, T6 heat treatment greatly improved the tensile properties of these alloy compositions due to the strengthening effect of the theta-Al2Cu phase. The elongation of these alloys generally decreases marginally with Mg content. The most significant property improvement of the alloys with higher Mg content is the substantial increase in wear resistance. This is attributed to the dispersion of smaller particles of Mg2Si and their coherence with the matrix as compared to the large Si particles in the conventional alloy. A new rheoforming process for A390 is presented that improves the processing of the semi-solid slurry. Structure modification elements were also added to refine the primary and eutectic silicon greatly improving the processing of the semi-solid slurry.