Change of Pattern of Solidification in Bottom Poured Ingots, Represented by a Mathematical Model and its Effect on the Appearance of Defects in Seamless Pipes of C.V.G. Sidor

"This paper shows a mathematical model based on finite elements, applied to bottom poured shell ingots of C.V.G. Sidor Plant. The model was used as a strategy to determine the thermal effects that are produced when solidification conditions are modified without interfering with the production process. The modification consisted of placing a thermal insulator on top of mould.The results obtained by the model indicated that the solidification time increases with insulator on base of the mould. With these results a significant number of casts were run with and without insulator. Latter by means of a metallurgical analysis it was determinated that the ingots cast with insulator reduce the level of non-metallic inclusions and the presence of internal blistering in seamless pipes.IntroductionThe process of fabrication of seamless pipes in SIDOR involves various steps of processing, such as heating the ingots, fabrication of the prelaminated, fabrication of the bored pipe, lamination of the pipe by passing through the pellegrine mill, heating the pipe in a walking bean furnace and final calibration through a calibrator mill. The material utilized for producing these pipes is provided entirely from a electrical arc furnace and casted ingots, especifically, from the superintendence of bottom pouring.The process of bottom pouring consists of positioning twelve moulds of diameters 415, 480 or 505 mm over a plate of grey cast iron in which exists a system of communicating vessels. The ingots are distributed around a central duct from which the steel flows down and filling gradually, each one of the moulds (Fig. 1)."