An Investigation On The High-Mg-Content Slag In Jinchuan Nickel Flash Smelting Furnace

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-Si02 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [m(Mgo)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, m(Fe)/m(SiO2) is 1.1-1.4 and the temperatures are within 1473?1773K, the slag viscosities increased with the increase of m(Mgo) and m(Fe)/m(sio,). When m(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When m(Mgo» 10%, the temperature should be kept above 1633K. When the content of MgO is higher, a lower viscosity slag ean be produced by decreasing the ratio of m(Fe)/m(sio,). The appropriate ratio of m(Fe)/m(sio,) for Jinchuan flash smelting furnace is about 1.2.