An Investigation Of The Reduction Of Eatery Paste (A12O3-As2O3-CaO-FeO-Fe2O3-PbO-Sb2O3-SiO2) Slags With Graphite

The reduction of a slag produced 6om the recycling of lead batteries was studied in a kilogram scale laboratory investigation by reacting with graphite at temperatures of 1180 and 1200°C. Simultaneous reduction of PbO, Fe203, Sb203 and As203 occurred with the Sb and As reporting to the metal while the lead content in the slag was above 2 wt%. The Sb and As distributions between metal and slag were strongly affected by temperature and slag oxidation state. The rates of reduction of PbO and Sb203 increased with increasing slag basicity and temperature and decreased as the PbO content in the slag decreased. The reduction rate of PbO from these slags was similar to other industrial lead slags at the same CaO/SiO2 ratio and temperature. The implications of the behavioural similarities of the antimonous slags during reduction with carbonaceous reductants and other lead slags are briefly discussed.