Alumina Surface Material from Aluminium Solid Waste and its Catalytic Application

"Treatment of industrial waste materials is created serious problem in Egypt. Aluminium sludge is generated as a by-product from aluminium household industry which contains significantly high alumina content exceeding 90%. This by-product randomly disposed and creates serious environment problems to locate community. To develop the treatment process of this material, the recovery of high purity alumina and identify the potential application is being the primary objective, This paper represents the recovery process of alumina process waste sludge High purity alumina material <99.8% aluminium oxide with originate particle size 0.125-0.420mm and apparent density 0.39g/cm3 was obtained with a specific surface area 139m2/g. Alumina produced was modified by cerium oxide doped alumina. The catalytic activity and selectivity was investigated in conversion of iso-propanol via dehydrogenation reaction yielding only acetone indicating an excellent selectivity the dehydrogenation. The presence of 10% CeO2 increase in the catalytic activity of 82% for the originated alumina. Introduction Approximately 20 thousand tons of aluminium waste produced in Egypt in 2006 with increasing amounts expected in succeeding years. A part of this waste contains organics impurities which coexisted with aluminium waste as a result of manufacture final aluminium products, waste usually content <1 to 2 wt% of organic carbon. It's generally admitted that the organic species are present in the form of lubricant oils used in rolling and pressing equipments for aluminium sheet. Both industry and government face possible high-cost disposal problems that more magnified by large volume of waste produced. The alumina recovery leachable study conduct in this paper had the following objectives: 1- Develop a process that can provide an environmentally acceptable residue and also recover the available alumina. 2- Evaluate the alumina produced in terms of grade and catalytic application."