Activities of Magnesium Oxide in the Nickel Oxide-Magnesium Oxide-Zinc Oxide System Using a Magnesium Fluoride Solid Electrolyte Galvanic Cell

The thermodynamic activities of MgO in the solid solutions that can exist in the system NiO-Mg0-Zn0 are determined by measuring the EMF of the cell: O2 (g), Pt / MgO, MgF2 // MgF2 // x MgO + yNiO + (1-x-y)ZnO / Pt, O2 (g) / MgF2 in the temperature range 1190-1237 K. Equilibrium phases were prepared along the quasi- binary lines MgO/NiO = 0.1765,0.3333, 1.0,3.0 and 5.667 with the ZnO contents being 0.1, 0.2, 0.25, 0.35, 0.5, 0.75 and 0.9. The crystal structures of the phases were identified by X-ray diffraction. Results obtained so far show that a single phase MgO-rich cubic solid solution exists upto 0.2 ZnO content and for compositions above 0.25 ZnO, a second ZnO rich wurtzite phase forms in addition. Activity measurements show that for low MgO and ZnO contents, the MgO activities exhibit ideal to slight positive deviation from ideality and at higher MgO contents, a negative deviation is shown. Further studies are in progress.