A Study of Carbon-Burdened and Cold-Bonded Pelletizing-Electrosmelting Process Disposing Low-Grade Manganese Ore

"The carbon-burdened and cold-bonded pelletizing-electrosmelting process is used to dispose low-grade manganese, and the qualified rich-manganese slag is obtained. On the condition that reduction roasting temperature was 1000?, reduction time was 45min, particle-size was -1mm, reductant dosage was 1.6%, basicity was 0.3, smelting temperature was 1410?, smelting time was 60min, it had a good effect on the melting between slag and metallographic phase, the manganese content was 32.58%, manganese recovery was 92.16% in the slag; while the iron content was 94.40%, iron recovery was 95.32% in the metallographic phase. It was proved by the demonstration tests.IntroductionManganese is an important raw material for steelmaking, which is extensively utilized in modern industry, the consumption of manganese for iron and steel industry accounts for 90% to 95%. After mining over 30 years, the high-grade manganese resources drop markedly, especially with the hypergrowth of steel industry, the domestic manganese is far from the requirement, as a result, we have to buy significant quantities of manganese overseas. Besides, the property of imported manganese is more and more complex, and the high-grade and lump manganese decrease year by year, while the fines and high-crystal water manganese are on the increase. Therefore, how to make effective use of domestic low-grade manganese and intensify the manganese’s smelting is an effective approach to reduce the cost of manganese series ferroalloy and improves market competitiveness[1-4]. It has important practical meaning."