A New Method for Investigation of Cold Rolling and Annealing Behavior of Low Carbon Steel Sheets Using Magnetic Properties

A new method to detect microstructural features such as recovery and recrystallization as well as cold rolling reduction in low carbon steels was developed based on magnetic hysteresis loop measurement. To this aim, a hysteresis loop measuring apparatus, specifically designed and assembled for plate samples was employed. It is shown that maximum field (Hmax) of hysteresis loop, measured at constant maximum flux density (Bmax) of 0.5T, is an adequatemagnetic property to monitor different stages of changing microstructures during annealing.