A Manufacture Process of New Type Tungstate and Hydrogen Reduetion of Tungsten Oxide Thereof

"In ordinary manufacture process of tungsten powder, a preferable intermediate product used is ammonium paratungstate (APT). The particle size of tungten powder made from it through W2OO58 is larger than 1. 0 um. In order to obtain ultrafine tungsten powder with narrow size distribution, a new type of tungstate, hydraziniull tungstate, was studied. Its formula is 5(N2H5)2O·12 WO.s , with tetragonal crystal structure of a=5.821 , c=18. 468. Three methods for preparing hydrazinium tungstate (ART) were set up and ART can be produced by current industrial APT process with little modification of operation and without any change of equipment.Under certain PH and operation condition of the solution from which ART was produced, an autoreduction of tungsten occured, which produced a lower valency tungstate with blue color when ART was heated at different temperatures, in N atmosphere, tungsten bronze, tetragonal W0290 and W02.7E could be obtained respectively. They all have the superiorities, in the production of tungsten powder, of superfine size and narrow size distribution [average size of 0.5um or even smaller.The rate of autoreduction of ART is very fast at elevated temperature. The reduction reaction, which gaves tetragonal WO290, could be handled smoothly without explosion. To research their behaviors at autoreduction temperatures and the products of autoreduction will be new advances of tungsten chemistry and may also serve tungsten industry with new processes and materials."